uygulama süresi

listen to the pronunciation of uygulama süresi
Турецкий язык - Английский Язык
pot life
The period of time a reacting composition remains suitable for its intended processing after mixing with reaction-initiating agents
Length of time in which a catalyzed thermosetting resin retains sufficiently low viscosity for processing
Generally defined as the time from mixing till the material has "gone off' in the container NB: This will differ from the applied material
The length of time a catalyzed thermosetting resin system retains a viscosity low enough for it to be suitable for processing
The length of time a mixed adhesive remains workable (flowable) before hardening
The length of time a paint material is useful after its original package is opened or a catalyst or other curing agent is added
period of time within which the coating can be applied, after the blending operation, before polymerization causes a viscosity increase which makes application impossible It is strongly affected by temperature (it decreases as temperature increases)
The time in which a paint is sprayable after mixing This usually refers to paint that has been mixed with a catalyst or activator This time can vary from a few minutes to several hours depending on the chemicals and the ambient temperature
The time it takes for a formulation to harden once two parts of an epoxy are mixed together The time depends on temperature, volume, and quantity of the mixture
The period of time during which a reacting polymeric compound remains suitable for its intended use after having been mixed with a reaction-initiating agent
The period of time, after mixing or the application of heat, that the material remains useable (pourable) in the particular application
The period during which a two-part paint can be applied after it has been mixed
The length of time during storage of an ink, emulsion, etc in a specific container under normal conditions without changing chemically and affecting usefulness
The useful life of a coating after mixing, Usually refers to paints which are mixed with a curing agent just before application Pot life may vary from minutes to hours, depending on the chemicals involved
The length of time an ink or emulsion can be stored in a specific container under normal conditions without changing chemically or affecting usefulness
The period of time during which a reacting thermosetting composition remains suitable for its intended processing after mixing with a reaction initiating agent
The amount of time a mixed material may be easily used at a specific temperature It Is usually measured as the time it takes for a material to double in viscosity